The basics of Italricambi manufacturing is strictly observed within many years of successful improvement and work. They allow to guarantee an excellent quality of Italricambi products:

1. High quality steel alloys
2. Fully automated production process providing the same high quality level for the full range of parts
3. Accurate quality controls

For this reason Italricambi s.p.a. provides a lifetime warranty against breakages for its products. 

 

 

 

Product quality and technical information: 

Bucket adapters  

Forged adapters

Steel alloy: 20MnCr6.3B
  • Resilience after heat treatment: about 50-70 J/cb.cm
  • Hardness range is included between: 42-47 HRC

Chemical composition

 

C

Mn

Cr

Si

Mo

B

P

S

Al

Ti

Cu

Ni

min

0,18

1,1

0,6

0,25

0

0,0005

0

0

0,02

0

0

0

max

0,23

1,3

0,08

0,35

0,08

0,0030

0,02

0,025

0,05

0,06

0,3

0,2

Cast adapters

  • Steel alloy: 20MnCrMoNi
  • Resilience after heat treatment: about >35 J/cb.cm
  • Hardness range is included between: 40-45 HRC 
  •  
  • Chemical composition

C

Mn

Cr

Si

Mo

P

S

Ni

min

0,18

0,85

0,4

0,15

0,15

0

0

0,4

max

0,23

1,15

0,6

0,35

0,25

0,035

0,04

0,7

 

Forged bucket tips / ripper points
Steel alloy: 30MnCrSiB4
Resilience after heat treatment: about 40-60 J/cb.cm
Hardness range is included between: 51-54 HRC

Chemical composition

C

Mn

Cr

Si

Mo

B

P

S

Al

Cu

Ni

min

0,31

1,1

1,0

1,3

0

0,001

0

0

0,020

0

0

max

0,35

1,3

1,2

1,3

0,05

0,003

0,02

0,02

0,035

0,3

0,2

 
Cast bucket tips / ripper points
Steel alloy: 30MnCrMoSi
Resilience after heat treatment: about >24 J/cb.cm
Hardness range is included between: 48-52 HRC

Chemical composition

C

Mn

Cr

Si

Mo

P

S

min

0,26

0,8

1,5

1,4

0,15

0

0

max

0,30

1,1

1,8

1,6

0,20

0,03

0,03

Cutting edges and end bits
Steel alloy: LB27MDB
Resilience after heat treatment: about 35-50 J/cb.cm
Hardness range is included between: 48-53 HRC

Chemical composition

C

Mn

Cr

Si

Mo

B

P

S

Al

Ti

Cu

Ni

min

0,26

1,1

0,3

0,15

0,15

0,001

0

0

0,0015

0,03

0

0

max

0,30

1,4

0,5

0,25

0,35

0,004

0,03

0,03

0,0040

0,005

0,4

0,3

Ripper shanks
Resilience after heat treatment: about 60-100 J/cb.cm
Hardness range is included between: 40-46 HRC

Chemical composition

C

Si

Mn

P

S

Cr

Mo

Ni

Cu

0,233

0,323

1,32

0,0113

0,0027

0,546

0,189

1,94

0,206

V

Al

Sn

B

Ti

W

Co

0,003

0,035

0,017

0,0007

0,005

0,01

0,007

 
Protectors
Resilience after heat treatment: about > 30 J/cb.cm
Hardness range is included between: 43-48 HRC

Chemical composition

C

Mn

Cr

Si

Mo

P

S

0,25

1,2

0,9

0,35

0,30

0,02

0,02

 